Powder pressed cuprous iodide (CuI) as a hole transporting material for perovskite solar cells
Uthayaraj, Siva; Karunarathne, DGBC; Kumara, GRA; Murugathas, Thanihaichelvan; Rasalingam, Shivatharsiny; Rajapakse, R.M.G.; Ravirajan, Punniyamoorthy; Velauthapillai, Dhayalan
Peer reviewed, Journal article
Published version

View/ Open
Date
2019Metadata
Show full item recordCollections
Original version
Uthayaraj, S., Karunarathne, D., Kumara, G., Murugathas, T., Rasalingam, S., Rajapakse, R., . . . Velauthapillai, D. (2019). Powder pressed cuprous iodide (CuI) as a hole transporting material for perovskite solar cells. Materials, 12(13), 1-9. 10.3390/ma12132037Abstract
This study focuses on employing cuprous iodide (CuI) as a hole-transporting material (HTM) in fabricating highly efficient perovskite solar cells (PSCs). The PSCs were made in air with either CuI or 2,2′,7,7′-Tetrakis[N,N-di(4-methoxyphenyl)amino]-9,9′-spirobifluorene (spiro-OMeTAD) as HTMs. A simple and novel pressing method was employed for incorporating CuI powder layer between perovskite layer and Pt top-contact to fabricate devices with CuI, while spiro-OMeTAD was spin-coated between perovskite layer and thermally evaporated Au top-contact to fabricate devices with spiro-OMeTAD. Under illuminations of 100 mW/cm2 with an air mass (AM) 1.5 filter in air, the average short-circuit current density (JSC) of the CuI devices was over 24 mA/cm2, which is marginally higher than that of spiro-OMeTAD devices. Higher JSC of the CuI devices can be attributed to high hole-mobility of CuI that minimizes the electron-hole recombination. However, the average power conversion efficiency (PCE) of the CuI devices were lower than that of spiro-OMeTAD devices due to slightly lower open-circuit voltage (VOC) and fill factor (FF). This is probably due to surface roughness of CuI powder. However, optimized devices with solvent-free powder pressed CuI as HTM show a promising efficiency of over 8.0 % under illuminations of 1 sun (100 mW/cm2) with an air mass 1.5 filter in air, which is the highest among the reported efficiency values for PSCs fabricated in an open environment with CuI as HTM.